| CHARACTERISTIC | STANDARD AS PER ISO-13006/2018 | OUR VALUE | TEST METHOD |
| REGULATORY PROPERTIES | |||
| Deviation in length & width | ± 0.3% | -0.03% | ISO-10545-2 |
| Deviation in Thickness | ± 5.0% | -0.03% | ISO-10545-2 |
| Deviation of Straightness in both side | ± 0.3% | 0.05% | ISO-10545-2 |
| Rectangularity | ± 0.3% | 0.05% | ISO-10545-2 |
| SURFACE FLATNESS | |||
| Centre Curvature | ± 0.4% | ± 0.04% | ISO-10545-2 |
| Edge Curvature of Length | ± 0.4% | ± 0.05% | ISO-10545-2 |
| Edge Curvature of Width | ± 0.4% | ± 0.05% | ISO-10545-2 |
| Surface Quality | As per mfg. | Min 95% | ISO-10545-2 |
| PHYSICAL PROPERTIES | |||
| Water absorption | 0.50% | 0.05% | ISO-10545-3 |
| Modulus of repture | 35 N/mm2 | Min. 36 N/mm2 | ISO-10545-4 |
| Breaking strength | Min. 1300 N | Min. 2100 N | ISO-10545-4 |
| Impact resistance | Min. 0.55 | Min. 0.83 | ISO-10545-5 |
| Surface abrasion resistance | As per mfg. | Min. Class-4 | ISO-10545-7 |
| Thermal expansion(COE) | As per mfg. | Max. 3.15 x 10-6 | ISO-10545-8 |
| Thermal shock resistance | No damage | No damage | ISO-10545-9 |
| Moisture expansion | Max 0.6 mm/n | 0.02 | ISO-10545-10 |
| Crazing Resistance | No damage | No damage | ISO-10545-11 |
| Frost resistance | No damage | No damage | ISO-10545-12 |
| Color difference | <0.75 | 0.4 | ISO-10545-16 |
| CHEMICAL PROPERTIES | |||
| Chemical resistance | No damage | No damage | ISO-10545-13 |
| Stain resistance | Resistant | Resistant | ISO-10545-14 |
| SAFETY PROPERTIES | |||
| Fire resistance | As per mfg. | Fireproof | N.A. |
| PROPERTIES | ISO Standard 13006/EN 176 Group BIa | OUR VALUE |
|---|---|---|
| Length and width | ± 0.5% | ± 0.4% |
| Thickness | ± 5.0% | ± 3.0% |
| Straightness of sides | ± 0.5% | ± 0.5% |
| Rectangularity | ± 0.6% | ± 0.4% |
| Surface flatness | ± 0.5% | ± 0.2% |
| Water absorption | ± 3.6% | ± 3.6% |
| Breaking strength | ≥ 220 Kgs/cm2 | ≥ 270 Kgs/cm2 |
| Resistance to chemicals | resistance to all alkalis (except hydrochloric acid and its compound) | resistance to all alkalis (except hydrochloric acid and its compound) |
| Thermal shock | 10 cycles | 4 cycles |
| PROPERTIES | TEST METHOD | ISO STANDARD 13006 B1a TILES | OUR VALUE |
|---|---|---|---|
| Length and width | BS EN ISO 10545-2 | ± 0.6% | ± 0.3% |
| Thickness | BS EN ISO 10545-2 | ± 5.0% | ± 3.0% |
| Straightness of sides | BS EN ISO 10545-2 | ± 0.5% | ± 0.3% |
| Rectangularity | BS EN ISO 10545-2 | ± 0.6% | ± 0.3% |
| Surface flatness | BS EN ISO 10545-2 | ± 0.5% | ± 0.3% |
| Water absorption | BS EN ISO 10545-3 | ≤ 0.5% | ≤ 0.05% |
| Breaking strength | BS EN ISO 10545-4 | ≥ 1300N | ≥ 1500N |
| Modulus of rupture | BS EN ISO 10545-4 | ≥ 35 N/mm2 | ≥ 45 N/mm2 |
| Resistance to deep abrasion | BS EN ISO 10545-6 | ≤ 175mm3 | ≤ 150mm3 |
| Linear thermal expansion | BS EN ISO 10545-8 | ≤ 9 x 10-6 °C1 | ≤ 7 x 10-6 °C1 |
| Thermal shock resistance | BS EN ISO 10545-9 | No visible defect | No visible defect |
| Frost resistance | BS EN ISO 10545-12 | Frost proof | Frost proof |
| Resistance to chemicals | BS EN ISO 10545-13 | No visible effect | No visible effect |
| Resistance to stains | BS EN ISO 10545-14 |
Manufacturer to state class |
Stains removed
Min. Class 3 |
| Colour resistance | BS EN ISO 10545-16 | No damage | No damage |
| Colour resistance to UV Light | DIN 51094 | No change in color | No change in color |
| Scratch hardness (MOH's Scale) | EN 101 | ≥ 6 MOHS | ≥ 7 MOHS |
| Surface quality | BS EN ISO 10545-2 | Min. 95% | No visible defect |
| Skid resistance (friction co-efficient) | BS EN ISO 10545-17 | > 0.4 | > 0.4 |
| Moisture Expansion | - | Nil | Nil |
| PROPERTIES | TEST METHOD | ISO Standard 13006/EN 176 Group BIa TILES | OUR VALUE |
|---|---|---|---|
| Length and width | BS EN ISO 10545-2 | ± 0.6% | ± 0.3% |
| Thickness | BS EN ISO 10545-2 | ± 5.0% | ± 3.0% |
| Straightness of sides | BS EN ISO 10545-2 | ± 0.5% | ± 0.3% |
| Rectangularity | BS EN ISO 10545-2 | ± 0.6% | ± 0.3% |
| Surface flatness | BS EN ISO 10545-2 | ± 0.5% | ± 0.3% |
| Water absorption | BS EN ISO 10545-3 | ≤ 0.5% | ≤ 0.05% |
| Breaking strength | BS EN ISO 10545-4 | ≥ 1300N | ≥ 1500N |
| Modulus of rupture | BS EN ISO 10545-4 | ≥ 35 N/mm2 | ≥ 45 N/mm2 |
| Resistance to deep abrasion | BS EN ISO 10545-6 | ≤ 175mm3 | ≤ 150mm3 |
| Linear thermal expansion | BS EN ISO 10545-8 | ≤ 9 x 10-6 °C1 | ≤ 7 x 10-6 °C1 |
| Thermal shock resistance | BS EN ISO 10545-9 | No visible defect | No visible defect |
| Frost resistance | BS EN ISO 10545-12 | Frost proof | Frost proof |
| Resistance to chemicals | BS EN ISO 10545-13 | No visible effect | No visible effect |
| Resistance to stains | BS EN ISO 10545-14 | Manufacturer to state class |
Stains removed
Min. Class 3 |
| Colour resistance | BS EN ISO 10545-16 | No damage | No damage |
| Colour resistance to UV Light | DIN 51094 | No change in color | No change in color |
| Scratch hardness (MOH's Scale) | EN 101 | ≥ 6 MOHS | ≥ 7 MOHS |
| Surface quality | BS EN ISO 10545-2 | Min. 95% | No visible defect |
| Skid resistance (friction co-efficient) | BS EN ISO 10545-17 | > 0.4 | > 0.4 |
| Moisture Expansion | - | Nil | Nil |
| PROPERTIES | TEST METHOD | ISO Standard 13006/EN 176 Group BIa | OUR VALUE |
|---|---|---|---|
| Deviation in Length | EN 98 | ± 0.6% | ± 0.1% |
| Deviation in Thickness | EN 98 | ± 5% | ± 4 % |
| Straightness of sides | EN 98 | ± 0.5% | ± 0.1% |
| Rectangularity | EN 98 | ± 0.6% | ± 0.2% |
| Surface flatness | EN 98 | ± 0.5% | ± 0.3% |
| Water absorption | EN 99 | < 0.5% | < 0.05% |
| Scratch hardness (MOH's Scale) | EN 101 | > 6 MOHS | > 7 MOHS |
| Modulus of Rupture | EN 100 | > 27 N/mm2 | > 47 N/mm2 |
| Abrasion Resistance | EN 102 | < 204 mm3 | < 98 mm3 |
| Skid Resistance (Friction Coefficient) | ASTM C-1028 | >0.4 | > 0.6 |
| Breaking Strength | ASTM C-648 | >1113 N | > 2830 N |
| Density (g/cc)* | DIN 51082 | > 2 | > 2.4 |
| Frost Resistance | EN 202 | Frost proof | Frost proof |
| Chemical Resistance | EN 106 | No damage | No damage |
| Thermal Shock Resistance | EN 104 | No damage | No damage |
| Colour Resistance | DIN 51094 | No damage | No damage |
| Thermal Expansion | EN 103 | < 9 x 10-6 | < 6 x 10-6 |
| Stain Resistance | ISO 10545-14 | Resistant | Resistant |
| Moisture Expansion | ISO 10545-10 | Nil | Nil |
| Glossiness* | Glossmeter | - | Min 65%-70% reflection |
| CHARACTERISTIC | STANDARD AS PER ISO-13006/ EN14411 GROUP Bla |
MEAN VALUE OF MAPS DOUBLE CHARGE VITRIFIED TILES |
TEST METHOD | |
| Regulatory Properties | Deviation In Length & Width | ± 0.5% | ± 0.10% | ISO-10545-2 |
| Deviation In Thickness | ± 5.00% | ± 2.00% | ISO-10545-2 | |
| Straightness of Sides | ± 0.50% | ± 0.10% | ISO-10545-2 | |
| Rectangularity | ± 0.50% | ± 0.10% | ISO-10545-2 | |
| Surface Flatness | ± 0.50% | ± 0.10% | ISO-10545-2 | |
| Color Differences | Unaltered | No Change | ISO-10545-16 | |
| Glossiness | As per Manufacture | Min.90 %* | Glossometer | |
| Surface Quality | Min.95% tiles should be free from visible defect |
Conforms | ISO 10545-2 | |
| Structural Properties | Water Absorption | ≤ 0.50 % | E ≤ 0.50% | ISO 10545-3 |
| Apparent Density | > 2.00 gm/cc | > 2.28 gm/cc | DIN 51082 | |
| Massive Mechanical Properties | Flexural Modulus Of Rupture | Min. 35N/mm² | Min. 40N/mm² | ISO-10545-4 |
| Flexural Breaking Strength | Min. 1300 N | Min. 2000 N | ISO-10545-4 | |
| Impact Resistance | As Per Manufacturer | Min. 0.55 | ISO-10545-5 | |
| Surface Mechanical Properties | Deep Abrasion Resistance | Max. 175mm³ | Max. 132mm³ | ISO-10545-6 |
| Moh's Hardnes | Min. 6 | ≥ 6 * | EN101 | |
| Thermo Hygrometric Properties | Frost Resistance | No. Damage | Frost Proof | ISO -10545-12 |
| Thermal Shock Resistance | No. Damage | No. Damage | ISO -10545-9 | |
| Moisture Expansion | Declared Value | Nil | ISO -10545-10 | |
| Thermal Expansion | Max.9.0 X 10-6 | Max. 6.5 X 10-6 | ISO -10545-8 | |
| Chemical Properties | Resistance of House Hold Chemical | No. Damage | No. Damage* | ISO -10545-13 |
| Stain Resistance | Resistance | Resistance* | ISO -10545-14 | |
| Safety Properties | Slip Resistance(friction Co Efficient) | >0.40 | >0.40 | ISO - 10545-17 |
| CHARACTERISTIC | STANDARD AS PER ISO-13006/2018 | OUR VALUE | TEST METHOD |
| REGULATORY PROPERTIES | |||
| Deviation in length & width | ± 0.3% | -0.03% | ISO-10545-2 |
| Deviation in Thickness | ± 5.0% | -0.03% | ISO-10545-2 |
| Deviation of Straightness in both side | ± 0.3% | 0.05% | ISO-10545-2 |
| Rectangularity | ± 0.3% | 0.05% | ISO-10545-2 |
| SURFACE FLATNESS | |||
| Centre Curvature | ± 0.4% | ± 0.04% | ISO-10545-2 |
| Edge Curvature of Length | ± 0.4% | ± 0.05% | ISO-10545-2 |
| Edge Curvature of Width | ± 0.4% | ± 0.05% | ISO-10545-2 |
| Surface Quality | As per mfg. | Min 95% | ISO-10545-2 |
| PHYSICAL PROPERTIES | |||
| Water absorption | 0.50% | 0.05% | ISO-10545-3 |
| Modulus of repture | 35 N/mm2 | Min. 36 N/mm2 | ISO-10545-4 |
| Breaking strength | Min. 1300 N | Min. 2100 N | ISO-10545-4 |
| Impact resistance | Min. 0.55 | Min. 0.83 | ISO-10545-5 |
| Surface abrasion resistance | As per mfg. | Min. Class-4 | ISO-10545-7 |
| Thermal expansion(COE) | As per mfg. | Max. 3.15 x 10-6 | ISO-10545-8 |
| Thermal shock resistance | No damage | No damage | ISO-10545-9 |
| Moisture expansion | Max 0.6 mm/n | 0.02 | ISO-10545-10 |
| Crazing Resistance | No damage | No damage | ISO-10545-11 |
| Frost resistance | No damage | No damage | ISO-10545-12 |
| Color difference | <0.75 | 0.4 | ISO-10545-16 |
| CHEMICAL PROPERTIES | |||
| Chemical resistance | No damage | No damage | ISO-10545-13 |
| Stain resistance | Resistant | Resistant | ISO-10545-14 |
| SAFETY PROPERTIES | |||
| Fire resistance | As per mfg. | Fireproof | N.A. |